Low Creep High Alumina Brick for Hot-blast Stove

  • AL2O3:75
  • Apparent Porosity %:20
  • Compress Strength, Mpa ≥:60
  • Creep Rate, % (0.2Mpa,50h)   :1550℃ 0.8
  • Linear Change after Reheating %:1550℃, 2h
Share With:
  
  • Overview
  • Technical Data
  • Inquiry
Low creep high alumina brick for blast furnace is made of corundum, mullite “sillimanite, andalusite and kyanite” and high quality bauxite clinker as raw material by shaping at high pressure and sintering at high temperature.
Characteristic:
1. The content of AL2O3 is ≥48%.
2. High refractoriness. The temperature is up to 1750~1790℃, it belongs to high-duty refractory.
3. High refractoriness under load. The URL is higher than fireclay brick as the high content of Al2O3, however, it is lower than silica brick because of mullite crystal does not form reticular tissue.
4. Excellent slag resistance. High alumina brick is a kind of neutral refractory material so it enjoys excellent resistance to acid slag and alkali slag corrosion.
Application:
The main markets for low creep high alumina brick are building lining of hot-blast stove, blast furnace, coke oven, rotary kilns of cement and so on.


Item

High Alumina Brick

 

DRL-155

DRL-150

DRL-145

DRL-140

DRL-135

DRL-130

DRL-127

AL2O3,%         ≥

75

75

65

65

65

60

50

Apparent Porosity,%  ≤

20

21

21

22

22

22

23

Bulk Density, g/cm3

2.65-2.85

2.65-2.85

2.50-2.70

2.40-2.60

2.35-2.30

2.30-2.50

2.30-2.50

Compress Strength, Mpa ≥

60

60

60

55

55

55

50

Creep Rate, %

1550

1500

1450

1400

1350

1300

1270

(0.2Mpa,50h)       ≤

0.8

0.8

0.8

0.8

0.8

0.8

0.8

Permanent Linear Change %

1550,2h

0.1-0.2

0.1-0.2

--

--

--

--

 

1450,2h

--

--

0.1-0.2

0.1-0.4

0.1-0.4

0.1-0.4

 

Please Feel free to give your inquiry in the form below.