• Fused Cast Zirconia Corundum Brick
  • Fused Cast Zirconia Corundum Brick

Fused Cast Zirconia Corundum Brick

  • True Specific Gravity :3.84 g/cm3
  • Apparent Porosity :1.2%
  • Exudation Temperature :1400℃
  • Static Corrosion (1500℃*36h):1.4mm/24h
Share With:
  
  • Overview
  • Technical Data
  • Inquiry
Besides the same eutectic with AC-33 Tile, AC-36 Tile has further strengthened anti-erosion ability and reduces the pollution of glass melt because more chain-shape zirconium oxide crystal and low glass phase content. It is suitable for the area with fast glass melt flow rate and high temperature, such as pool wall tiles of the melting tank, pavement tiles and charging mouth tiles ture of Fused Cast Zirconia Corundum Brick AC-33 enables it to have very good corrosion resistance to molten glass. It very rarely results in stoning and has very limited chances to cause blistering and other defects to glass, so AC-33 is the most common product used in the glass furnace.
 
AC-33
Besides the same eutectic with AC-33 Tile, AC-36 Tile has further strengthened anti-erosion ability and reduces the pollution of glass melt because more chain-shape zirconium oxide crystal and low glass phase content. It is suitable for the area with fast glass melt flow rate and high temperature, such as pool wall tiles of the melting tank, pavement tiles and charging mouth tiles.
AC-36

Fused Cast Zirconia Corundum Brick AC-41 has the most free baddeleyite crystals among the AZS families, which are evenly distributed within the block. Its corrosion resistibility is the best and thus it is usually recommended to be used in the most demanding positions to balance the furnace life.
AC-41



Item Fused Cast Zirconia Corundum Brick
AC-33
True SpecificGravity 3.84g/cm3
Apparent Porosity 1.2%
Cold Crushing Strength 350Mpa
Exudation Temperature 1400℃
Static Corrosion(1500℃*36h) 1.45mm/24h

Item Fused Cast Zirconia Corundum Brick
AC-36
True Specific Gravity 3.93g/cm3
Apparent Porosity 1.0%
Cold Crushing Strength 350Mpa
Exudation Temperature 1400℃
Static Corrosion(1500℃*36h) 1.4mm/24h


Item Fused Cast Zirconia Corundum Brick
AC-41
True Specific Gravity 4.1g/cm3
Apparent Porosity 0.9%
Cold Crushing Strength 350Mpa
Exudation Temperature 1400℃
Static Corrosion(1500℃*36h) 1.2mm/24h